Polytetrafluoroethylene Pipe Factory Direct Raw Material Polymer Synthetic Resin Seal with Powder Df203

• Customization: Available
• CAS No.: Qfreon
• Formula: Qfreon
• Model NO.: Ptfe powder 203
• EINECS: Qfreon
• Molecular Principal Chain: Element Organic Polymer
• Color: White Powder
• Type: Synthetic Resin and Plastics
• Keywords: PTFE Sheet
• Processing Method: by Moulding Pressure
• Purity: 99.9%
• Application: PTFE Gasket, Rod, Tube, Sheet, Bearings
• MOQ: 100
• Transport Package: 20kg
• Specification: 20KG
• Trademark: QFREON OR OEM
• Origin: Shandong, China

Product Description

 

 

 

ltem	unit	DF-203F
Appearance	/	scrap metal, sand and other impurities cannot be mixed, with visible dark spots cannot exceed 2%
Bulk Density,g/l	/	475±100
Tensile strength,≥	Mpa	24
Elongation at break,≥	%	300
Relative density	/	2.150-2.200
Moisture Content,%≤	%	0.030
Average Particle SIze	/	400-575
Maximum compression ratio	/	4001
Hot stress crack resistance	/	- -

 

Polytetrafluoroethylene (PTFE), commonly known as "the king of plastics", is a polymer compound formed by the polymerization of PTFE. Insulation and good resistance to aging. Used as engineering plastics, can be made into PTFE tube, rod, tape, plate, film, etc. Generally used in corrosion-resistant pipes, containers, pumps, valves, radars, high-frequency communication equipment, and radio equipment with high performance requirements. Processing method   Molding Main Application The resin are mainly used as insulating film for electric, the products of thin wall, seal, gasket, club, panel, tube, axletree, seal ring, and loop etc Package, transportation and storage 1). PTFE is packed in double layer PVC bags inside and in hard circular barrels outside.20kg/barrel. On the barrel, there should be attached label and quality certificate. 2). PTFE should be stored in clean dry warehouse to prevent from dust, moisture, etc, foreign maters. 3). The product are transported according to non-dangerousproducts. Heat, moisture, freezing and strong shock should be avoided during transportation. Over-bumpiness and compression is adapt to make the resin bind together.